CO oxidation over Au/TiO2 catalyst: Pretreatment effects, catalyst deactivation, and carbonates production

Johnny Saavedra, Camilah Powell, Basu Panthi, Christopher J. Pursell, Bert D. Chandler

Research output: Contribution to journalArticlepeer-review

65 Scopus citations


A commercially available Au/TiO2 catalyst was subjected to a variety of thermal treatments in order to understand how variations in catalyst pretreatment procedures might affect CO oxidation catalysis. Catalytic activity was found to be inversely correlated to the temperature of the pretreatment. Infrared spectroscopy of adsorbed CO experiments, followed by a Temkin analysis of the data, indicated that the thermal treatments caused essentially no changes to the electronics of the Au particles; this, and a series of catalysis control experiments, and previous transmission electron microscopy (TEM) studies ruled out particle growth as a contributing factor to the activity loss. Fourier transform infrared (FTIR) spectroscopy showed that pretreating the catalyst results in water desorption from the surface, but the observable water loss was similar for all the treatments and could not be correlated with catalytic activity. A Michaelis-Menten kinetic treatment indicated that the main reason for deactivation is a loss in the number of active sites with little changes in their intrinsic activity. In situ FTIR experiments during CO oxidation showed extensive buildup of carbonate-like surface species when the pretreated catalysts were contacted with the feed gas. A semi-quantitative infrared spectroscopy method was developed for comparing the amount of carbonates present on each catalyst; results from these experiments showed a strong correlation between the steady-state catalytic activity and amount of surface carbonates generated during the initial moments of catalysis. Further, this experimental protocol was used to show that the carbonates reside on the titania support rather than on the Au, as there was no evidence that they poison Au-CO binding sites. The role of the carbonates in the reaction scheme, their potential role in catalyst deactivation, and the role of surface hydroxyls and water are discussed.

Original languageEnglish
Pages (from-to)37-47
Number of pages11
JournalJournal of Catalysis
StatePublished - 13 Aug 2013
Externally publishedYes


  • Carbonates Au/TiO
  • CO adsorption
  • CO oxidation
  • Deactivation
  • Heat of adsorption
  • IR spectroscopy
  • Michaelis-Menten kinetics
  • Pretreatment
  • Temkin adsorption

ASJC Scopus subject areas

  • Catalysis
  • Physical and Theoretical Chemistry


Dive into the research topics of 'CO oxidation over Au/TiO2 catalyst: Pretreatment effects, catalyst deactivation, and carbonates production'. Together they form a unique fingerprint.

Cite this