Contribution to the uranium-gallium phase diagram

S. Salhov, G. Kimmel, M. P. Dariel

Research output: Contribution to journalArticlepeer-review

10 Scopus citations


Uranium-rich gallium alloys were studied by metallography, electron microscopy, X-ray diffraction and differential thermal analysis. Gallium additions allow retaining metastable β-uranium alloys at ambient temperature. The solubility of Ga in the high temperature uranium phases was determined by WDS, reaches 8 at.% at 800 °C in Uγ and 1.2 at.%, in Uβ at 720 °C. The presence of the Ga5U3 compound, structure type Pd5Pu3, was confirmed. Moderate mechanical stresses at room temperature promote the transformation of the metastable Uβ alloys into Uα′ by a shear-like transformation. The latter is a Ga-containing metastable variant of the room temperature equilibrium uranium allotrope. The matastable structure ultimately reverts to the equilibrium Uα and releases excess Ga by precipitation of the U3Ga5 compound in the form of thin platelets.

Original languageEnglish
Pages (from-to)257-260
Number of pages4
JournalJournal of Alloys and Compounds
Issue numberSPEC. ISS.
StatePublished - 1 Nov 2007


  • Actinide alloys and compounds
  • Metastable structures
  • Phase diagrams
  • Quenching
  • Solubility limits

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry


Dive into the research topics of 'Contribution to the uranium-gallium phase diagram'. Together they form a unique fingerprint.

Cite this