Effect of annealing temperature and cadmium doping on structure and magnetic properties of neodymium orthoferrite nanoparticles synthesized by a simple co-precipitation method

Keyphrases

• Nanoparticles 100%
• Magnetic Properties 100%
• Structure-property Relationships 100%
• Annealing Temperature 100%
• Nanopowder 100%
• Neodymium 100%
• Orthoferrites 100%
• Annealing Temperature Effect 100%
• Simple Co-precipitation Method 100%
• Cadmium Doping 100%
• Aqueous Solution 50%
• Annealing 50%
• Particle Size 50%
• Surfactant 50%
• Fe(III) 50%
• Hydroxide 50%
• SEM Analysis 50%
• Nitrate 50%
• Remanent Magnetization 50%
• Saturation Magnetization 50%
• Hard Disk Drive 50%
• Nd(III) 50%
• Boiling Water 50%
• Percent Sodium 50%
• Permanent Magnet 50%
• Cadmium Concentration 50%
• Coercivity 50%
• In Situ TEM 50%
• Cd(II) 50%
• Permanent Magnetic 50%
• Average Crystallite Size 50%
• High Coercivity 50%
• Magnetic Recording 50%
• Rare Earth Perovskites 50%
• LaFe1-xTixO3 50%

Material Science

• Annealing 100%
• Nanoparticle 100%
• Magnetic Property 100%
• Neodymium 100%
• Cadmium 100%
• Coprecipitation 100%
• Nanopowder 66%
• Surface Active Agent 33%
• Scanning Electron Microscopy 33%
• Sodium 33%
• X-Ray Diffraction 33%
• Crystallite Size 33%