Abstract
Effect of dimethyl sulfoxide (DMSO) on the electrical properties of PEDOT:PSS/n-Si heterojunction diodes has been studied. Poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS) was deposited on n-type Si wafer using facile process of spin coating. The DMSO content was varied from 0 to 8 vol%. Electrical characterization of these heterojunction diodes as performed using both current-voltage (I-V) and capacitance-voltage (C-V) measurements. All diodes showed rectifying behavior. AFM measurement revealed that the surface became more rough after the DMSO treatment of PEDOT:PSS films. The RMS values were found in the range of 4-6 nm. The resistivity of the PEDOT:PSS films decreased with increase in temperature. The addition of DMSO into PEDOT:PSS solution results in a decrease in resistivity of films by approximately two orders of magnitude. PEDOT:PSS films showed high transmission more than 85% in the entire visible region. Raman spectroscopy indicated effect of the DMSO treatment on the chemical structure of PEDOT chains, suggesting a conformational change of PEDOT chain in the film. An optimal value of DMSO was obtained with 5 vol% content, and it showed the best PEDOT:PSS films properties and good quality heterojunction diodes characteristics with ideality factor of 2.4 and barrier height 0.80 eV.
| Original language | English |
|---|---|
| Pages (from-to) | 528-534 |
| Number of pages | 7 |
| Journal | Current Applied Physics |
| Volume | 15 |
| Issue number | 4 |
| DOIs | |
| State | Published - 1 Jan 2015 |
| Externally published | Yes |
Keywords
- DMSO
- Electrical properties
- Heterojunction
- PEDOT:PSS
- Resistivity
ASJC Scopus subject areas
- General Materials Science
- General Physics and Astronomy
Fingerprint
Dive into the research topics of 'Effect of dimethyl sulfoxide on the electrical properties of PEDOT:PSS/n-Si heterojunction diodes'. Together they form a unique fingerprint.Cite this
- APA
- Author
- BIBTEX
- Harvard
- Standard
- RIS
- Vancouver