Effect of temperature, strain, and strain rate on the flow stress of aluminum under shock-wave compression

E. B. Zaretsky, G. I. Kanel

Research output: Contribution to journalArticlepeer-review

94 Scopus citations

Abstract

The evolution of elastic-plastic shock waves with the propagation distance has been studied in 99.99% purity aluminum and in annealed 6061 aluminum alloy. The free surface velocity histories of shock-loaded samples, 0.1-2.0 mm thick and with initial temperature from 296 to 932 K, have been recorded using velocity interferometer system for any reflector (VISAR). The measured amplitudes of the elastic precursor waves have been approximated by power functions of the propagation distance, and these data have been converted into relationships between the shear stress at the top of elastic precursor wave and the initial plastic strain rate. The latter was found to decrease from 10 6 to 10 4 s -1 over 0.1 to 2-mm precursor traverse, while the density of mobile dislocations corresponding to these strain rates varied from 2 × 10 8 to 5 × 10 6 cm -2. At fixed strain rates, the flow stress of aluminum grows linearly with temperature. An analysis of the rise times of the plastic shock waves has shown that, for the same level of shear stress, the plastic strain rate at the shock front is by an order of magnitude higher and the density of mobile dislocations is 2-3 times higher than their initial values behind the elastic precursor front.

Original languageEnglish
Article number073504
JournalJournal of Applied Physics
Volume112
Issue number7
DOIs
StatePublished - 1 Oct 2012

Fingerprint

Dive into the research topics of 'Effect of temperature, strain, and strain rate on the flow stress of aluminum under shock-wave compression'. Together they form a unique fingerprint.

Cite this