T1 - Low level laser irradiation stimulates osteogenic phenotype of mesenchymal stem cells seeded on a three-dimensional biomatrix
AU - Abramovitch-Gottlib, Liat
AU - Gross, Talia
AU - Naveh, Doron
AU - Geresh, Shimona
AU - Rosenwaks, Salman
AU - Bar, Ilana
AU - Vago, Razi
N1 - Funding Information:
seeding in three separated experiment sets. Dark areas represent bone nodules formation. Calibration line represents 500 µm aggregates in fat tissue. No differences in fat formation were detected during all experimental period. Calibration line represents 500 µm Fig. 7 Alkaline phosphatase (ALP) activity normalized to total protein concentration of MSCs seeded on 3D biomatrices without (magenta columns) and with (blue columns) LLLI. Analyses were performed 1–7, 10, 14, 21 and 28 days after seeding. (In each time interval (n = 5) bars represent means ± SD; Student’s t-test: (*) p < 0.05; (**) p < 0.01) Acknowledgments The research was partially supported by the Binational Science Foundation (BSF) # 2001045 and by the James Franck Binational German-Israeli Program in Laser-Matter Interaction. The authors are grateful to Mrs. Aviva Kiryati for expert assistance in SEM and EDS analyses. The authors wish to thank Mrs. Inez Murinek for the fruitful discussions and comments on the manuscript.
PY - 2005/12/1
Y1 - 2005/12/1
N2 - Mesenchymal stem cells (MSCs) seeded on three-dimensional (3D) coralline (Porites lutea) biomatrices were irradiated with low-level laser irradiation (LLLI). The consequent phenotype modulation and development of MSCs towards ossified tissue was studied in this combined 3D biomatrix/LLLI system and in a control group, which was similarly grown, but was not treated by LLLI. The irradiated and non irradiated MSC were tested at 1-7, 10, 14, 21, 28 days of culturing via analysis of cellular distribution on matrices (trypan blue), calcium incorporation to newly formed tissue (alizarin red), bone nodule formation (von Kossa), fat aggregates formation (oil red O), alkaline phosphatase (ALP) activity, scanning electron microscopy (SEM) and electron dispersive spectrometry (EDS). The results obtained from the irradiated samples showed enhanced tissue formation, appearance of phosphorous peaks and calcium and phosphate incorporation to newly formed tissue. Moreover, in irradiated samples ALP activity was significantly enhanced in early stages and notably reduced in late stages of culturing. These findings of cell and tissue parameters up to 28 days of culture revealed higher ossification levels in irradiated samples compared with the control group. We suggest that both the surface properties of the 3D crystalline biomatrices and the LLLI have biostimulatory effects on the conversion of MSCs into bone-forming cells and on the induction of ex-vivo ossification.
AB - Mesenchymal stem cells (MSCs) seeded on three-dimensional (3D) coralline (Porites lutea) biomatrices were irradiated with low-level laser irradiation (LLLI). The consequent phenotype modulation and development of MSCs towards ossified tissue was studied in this combined 3D biomatrix/LLLI system and in a control group, which was similarly grown, but was not treated by LLLI. The irradiated and non irradiated MSC were tested at 1-7, 10, 14, 21, 28 days of culturing via analysis of cellular distribution on matrices (trypan blue), calcium incorporation to newly formed tissue (alizarin red), bone nodule formation (von Kossa), fat aggregates formation (oil red O), alkaline phosphatase (ALP) activity, scanning electron microscopy (SEM) and electron dispersive spectrometry (EDS). The results obtained from the irradiated samples showed enhanced tissue formation, appearance of phosphorous peaks and calcium and phosphate incorporation to newly formed tissue. Moreover, in irradiated samples ALP activity was significantly enhanced in early stages and notably reduced in late stages of culturing. These findings of cell and tissue parameters up to 28 days of culture revealed higher ossification levels in irradiated samples compared with the control group. We suggest that both the surface properties of the 3D crystalline biomatrices and the LLLI have biostimulatory effects on the conversion of MSCs into bone-forming cells and on the induction of ex-vivo ossification.
KW - Biomaterials
KW - Coral
KW - Low-level laser irradiation
KW - Mesenchymal stem cells
KW - Osteogenesis
UR - http://www.scopus.com/inward/record.url?scp=29144525995&partnerID=8YFLogxK
U2 - 10.1007/s10103-005-0355-9
DO - 10.1007/s10103-005-0355-9
M3 - Article
AN - SCOPUS:29144525995
SN - 0268-8921
VL - 20
SP - 138
EP - 146
JO - Lasers in Medical Science
JF - Lasers in Medical Science
IS - 3-4
ER -