Keyphrases
Catastrophic Failure
100%
Microstructure Modification
100%
Main Landing Gear
100%
Fluorescent Particles
33%
Failure Mechanism
33%
Overhaul Process
33%
Particle Inspection
33%
Microhardness
16%
Mechanism-based
16%
Initiation Mechanism
16%
Structural Materials
16%
Strong Impact
16%
Left Main
16%
Fracture Surface
16%
Airplane
16%
Crack Propagation
16%
Chemical Analysis
16%
Visual Inspection
16%
Crack Initiation
16%
Failure Analysis
16%
Boeing
16%
Ground Crew
16%
Stress Corrosion Cracking
16%
Hydrogen Content
16%
Hydrogen Embrittlement
16%
Fracture Mode
16%
Lateral Movement
16%
Take-off
16%
Loud Noise
16%
Embrittlement
16%
Grinding Process
16%
Vertical Movement
16%
Intergranular Fracture
16%
Propagation Stage
16%
Side Arm
16%
Microstructure Change
16%
Ministry of Transport
16%
Mode Classification
16%
Hydrogen Fatigue
16%
Microetching
16%
Barkhausen
16%
Steel 4340
16%
Chief Investigator
16%
Gear Fault
16%
High-strength Low-alloy (HSLA) Steel
16%
Flight Crew
16%
Takeoff Flight
16%
Engineering
Microstructure
100%
Grinding (Machining)
100%
Catastrophic Failure
100%
Landing Gear
100%
Failure Mechanism
33%
Fracture Surface
16%
Visual Inspection
16%
Failure Analysis
16%
Aircraft
16%
Microhardness
16%
Hydrogen Embrittlement
16%
Stress Corrosion Cracking
16%
Structural Materials
16%
Embrittlement
16%
Back Side
16%
Intergranular Fracture
16%
High-Strength Low-Alloy Steel
16%