Multifilamentary Nb-Nb3 (Al,Ge) superconductors

M. R. Pickus; M. P. Dariel; J. T. Holthuis; J. Ling Fai Wang; J. Granda

doi:10.1063/1.88958

Multifilamentary Nb-Nb₃ (Al,Ge) superconductors

M. R. Pickus, M. P. Dariel, J. T. Holthuis, J. Ling Fai Wang, J. Granda

Research output: Contribution to journal › Article › peer-review

9 Scopus citations

Abstract

Multifilamentary Nb-Nb₃ (Al,Ge) superconductors were prepared using an infiltration process. The critical temperature of sample diffusion reacted in the 1250-1700°C temperature interval ranged from 16 to 19.0°K. A critical current density of 10⁵ A/cm² at 50 kOe was observed for samples reacted at lower temperatures.

Original language	English
Pages (from-to)	810-812
Number of pages	3
Journal	Applied Physics Letters
Volume	29
Issue number	12
DOIs	https://doi.org/10.1063/1.88958
State	Published - 1 Dec 1976
Externally published	Yes

ASJC Scopus subject areas

Physics and Astronomy (miscellaneous)

Access to Document

10.1063/1.88958

Cite this

@article{fb7c25b93eb841729975f124611d1f32,

title = "Multifilamentary Nb-Nb3 (Al,Ge) superconductors",

abstract = "Multifilamentary Nb-Nb3 (Al,Ge) superconductors were prepared using an infiltration process. The critical temperature of sample diffusion reacted in the 1250-1700°C temperature interval ranged from 16 to 19.0°K. A critical current density of 105 A/cm2 at 50 kOe was observed for samples reacted at lower temperatures.",

author = "Pickus, {M. R.} and Dariel, {M. P.} and Holthuis, {J. T.} and Wang, {J. Ling Fai} and J. Granda",

year = "1976",

month = dec,

day = "1",

doi = "10.1063/1.88958",

language = "English",

volume = "29",

pages = "810--812",

journal = "Applied Physics Letters",

issn = "0003-6951",

publisher = "American Institute of Physics",

number = "12",

}

TY - JOUR

T1 - Multifilamentary Nb-Nb3 (Al,Ge) superconductors

AU - Pickus, M. R.

AU - Dariel, M. P.

AU - Holthuis, J. T.

AU - Wang, J. Ling Fai

AU - Granda, J.

PY - 1976/12/1

Y1 - 1976/12/1

N2 - Multifilamentary Nb-Nb3 (Al,Ge) superconductors were prepared using an infiltration process. The critical temperature of sample diffusion reacted in the 1250-1700°C temperature interval ranged from 16 to 19.0°K. A critical current density of 105 A/cm2 at 50 kOe was observed for samples reacted at lower temperatures.

AB - Multifilamentary Nb-Nb3 (Al,Ge) superconductors were prepared using an infiltration process. The critical temperature of sample diffusion reacted in the 1250-1700°C temperature interval ranged from 16 to 19.0°K. A critical current density of 105 A/cm2 at 50 kOe was observed for samples reacted at lower temperatures.

UR - http://www.scopus.com/inward/record.url?scp=9244227718&partnerID=8YFLogxK

U2 - 10.1063/1.88958

DO - 10.1063/1.88958

M3 - Article

AN - SCOPUS:9244227718

SN - 0003-6951

VL - 29

SP - 810

EP - 812

JO - Applied Physics Letters

JF - Applied Physics Letters

IS - 12

ER -

Multifilamentary Nb-Nb₃ (Al,Ge) superconductors

Abstract

ASJC Scopus subject areas

Access to Document

Other files and links

Fingerprint

Cite this