Niobium layers on graphite: Growth parameters and thermal annealing effects

S. Barzilai, N. Frage, A. Raveh

Research output: Contribution to journalArticlepeer-review

16 Scopus citations

Abstract

Thin films of niobium (∼8 μm thick) were deposited on an ATJ graphite substrate by radio-frequency magnetron sputtering at low temperatures (420plusmn;50 K) under argon pressure of 0.67 Pa. After deposition, the layers were thermally annealed in a vacuum of 6.67 × 10-4 Pa at temperatures of 1073-2073 K for 10 to 480 min. Nb2C and NbC phases were identified by X-ray diffraction after the thermal annealing, scanning electron microscopy and wavelength dispersive analyses. The carbide layer thicknesses were measured and the growth rate constants were determined at different temperatures. It was found that the activation energies are 190 kJ/mol for Nb2C, 164 kJ/mol for NbC, and 169.4 kJ/mol for the combined carbide layers. This study also presents the specific features of phase formation, adhesion and microhardness of the carbide layers.

Original languageEnglish
Pages (from-to)4646-4653
Number of pages8
JournalSurface and Coatings Technology
Volume200
Issue number14-15
DOIs
StatePublished - 10 Apr 2006

Keywords

  • Graphite
  • Interdiffusion
  • Niobium
  • Sputtering
  • Thermal annealing

Fingerprint

Dive into the research topics of 'Niobium layers on graphite: Growth parameters and thermal annealing effects'. Together they form a unique fingerprint.

Cite this