TY - JOUR
T1 - Water Transport and Thermomechanical Properties of Ti3C2T z MXene Epoxy Nanocomposites
AU - Carey, Michael S.
AU - Sokol, Maxim
AU - Palmese, Giuseppe R.
AU - Barsoum, Michel W.
N1 - Publisher Copyright:
© 2019 American Chemical Society.
PY - 2019/10/23
Y1 - 2019/10/23
N2 - Herein, we present the fabrication of dispersed, 5.0 wt % (1.74 vol %) Ti3C2Tz MXene epoxy nanocomposites (NCs), and report on their water transport and mechanical properties. To make the composites, Li+ ions between Ti3C2Tz MXene multilayers, MLs, present after the etching step were exchanged with either 12-aminolauric acid, ALA, or di(hydrogenated tallow)benzyl methyl ammonium chloride, DHT. After drying, the resulting ML powders were added at room temperature to the epoxy resin (diglycidyl ether of bisphenol A), followed by the curing agent, triethylenetetramine. The NCs were characterized by X-ray diffraction, thermogravimetric analysis, dynamic vapor sorption, dynamic mechanical analysis, scanning and transmission electron microscopies, and infrared spectroscopy. From XRD, the lack of signature MXene basal peaks, as well as evidence of exfoliation supported by TEM micrographs, we conclude that the MXene ML had indeed been intercalated by the epoxy. The distribution of the exfoliated multilayers, MLs, however, was not uniform. Nevertheless, our relative permeabilities, with a 1.74 vol % loading, are 5 times lower than results obtained in the carbon- or clay-reinforced epoxy NC literature. The lower permeabilities are due to reductions in both solubilities and diffusivities relative to the neat polymer. In the case of DHT, the water solubility at all temperatures was almost halved. The mechanical properties and thermal stability are found to be slightly improved with the addition of DHT-MXene. As far as we are aware, this is the first report of exfoliation of MXene in an epoxy matrix. Additionally, this study is the first to measure the diffusion of water in MXene epoxy NCs. More work on better dispersion of the MLs is indicated and ongoing.
AB - Herein, we present the fabrication of dispersed, 5.0 wt % (1.74 vol %) Ti3C2Tz MXene epoxy nanocomposites (NCs), and report on their water transport and mechanical properties. To make the composites, Li+ ions between Ti3C2Tz MXene multilayers, MLs, present after the etching step were exchanged with either 12-aminolauric acid, ALA, or di(hydrogenated tallow)benzyl methyl ammonium chloride, DHT. After drying, the resulting ML powders were added at room temperature to the epoxy resin (diglycidyl ether of bisphenol A), followed by the curing agent, triethylenetetramine. The NCs were characterized by X-ray diffraction, thermogravimetric analysis, dynamic vapor sorption, dynamic mechanical analysis, scanning and transmission electron microscopies, and infrared spectroscopy. From XRD, the lack of signature MXene basal peaks, as well as evidence of exfoliation supported by TEM micrographs, we conclude that the MXene ML had indeed been intercalated by the epoxy. The distribution of the exfoliated multilayers, MLs, however, was not uniform. Nevertheless, our relative permeabilities, with a 1.74 vol % loading, are 5 times lower than results obtained in the carbon- or clay-reinforced epoxy NC literature. The lower permeabilities are due to reductions in both solubilities and diffusivities relative to the neat polymer. In the case of DHT, the water solubility at all temperatures was almost halved. The mechanical properties and thermal stability are found to be slightly improved with the addition of DHT-MXene. As far as we are aware, this is the first report of exfoliation of MXene in an epoxy matrix. Additionally, this study is the first to measure the diffusion of water in MXene epoxy NCs. More work on better dispersion of the MLs is indicated and ongoing.
KW - MXene
KW - barrier properties
KW - epoxy
KW - nanocomposite
KW - polymer
UR - http://www.scopus.com/inward/record.url?scp=85073169135&partnerID=8YFLogxK
U2 - 10.1021/acsami.9b11448
DO - 10.1021/acsami.9b11448
M3 - Article
C2 - 31539221
AN - SCOPUS:85073169135
SN - 1944-8244
VL - 11
SP - 39143
EP - 39149
JO - ACS Applied Materials and Interfaces
JF - ACS Applied Materials and Interfaces
IS - 42
ER -